• Testing materials
  • Flexbar 16117
  • Flexbar 15158
  • 复制胶
  • Service
  • Zero Stock
  • Hard-To-Find Materials
  • Consignment Sales
  • Value-Added Service
  • Technical Support
  • Applications
  • Applications in Oil & Gas Industry
  • Artificial Lift
  • Completion
  • Drilling
  • Subsea Equipment
  • Applications in Electronics Industry
  • uedbet提款uedbet官网下载软件和uedbet提款箔
  • 电子电气
  • Articles
  • Alloying elements of stainless steel
  • Status of stainless steel(Temper)
  • Super alloy for key applications in oil and gas industry--MP35N
  • Price VS Quality
  • ROHS
  • DFARS
  • MSDS
  • About Us
  • About Us
  • News
  • Contact Us
  • Products

    Eaton Alloys PTE LTD. was established in 2011 (as Eaton Alloys Limited) and has grown consistently over this time to become a specialized supplier for specialty metals widely used in oil a

    Online Documents

    Data Sheets & Technical Documents

    Download articles

    Products

    Online Documents

    Data Sheets & Technical Documents

    Download articles





    Singapore

    Add.: 139 Bedok North Avenue 3, #10-188, Singapore 460139
    Tel: 0065 9664 4411
    Email:tony@eatonalloys.com

    Web:www.eatonalloys.com

    China

    Add.: 489# Guanghua Dong 3rd Road, Chengdu, China, 610091
    Tel: 0086 28 81703462
    Email: sales@eatonalloys.com
    Web: www.eatonalloys.com


    925Alloy

     
    925合金
    UNS N09925, NACE MR0175
     
    925合金是一种可时效硬化的镍铁铬合金,既耐腐蚀又具有很高的强度。镍和铜、钛、钼和铝结合,提供了对应力腐蚀开裂,坑蚀,缝隙腐蚀,氧化和还原环境的抵抗力,因此广泛用于井下,表面气井部件,轴产品和紧固件。
     
    化学成分
     
    0.03%
    0.030%
    19.50-23.50%
    2.50-3.50%
    1.90-2.40%
    0.10-0.50%
    锰  1.00%
    0.50%
    38.00-46.00%
    1.50-3.00%
    钶/铌 0.50%
    22.00%
     
     
    耐腐蚀性能
     
    925合金在氧化环境和还原环境都能耐受多种腐蚀,特别适用于高温高压的酸性气井,可抵抗5%NaCl+0.5%乙酸+饱和H2S溶液环境导致的开裂。
     
    物理性质
     
    密度: 0.292 lb/in3
    平均比热:
    \
    \
    导热率
    \
    \
    泊松比 0.293
    弹性模量(E) (70°F) 28.9 X 103 ksi
    电阻 701.0 ohm-cir-mil/ft
    熔距 2390-2490°F
     
     
    机械性能
     
    夏比V型缺口冲击测试-固溶退火并时效
    \
     
    升温环境的抗拉强度
    \
     
    抗拉强度-固溶处理并时效
    \
     
     
    热处理
     
    925合金常见的供货状态为固溶退火态和固溶+时效状态。该材料的固溶处理是加热至1800-1900°F, 30分钟-4个小时,然后水淬。时效处理是在1365°F保温8个小时,然后炉冷到1150°F,保温6个小时,然后空冷。
     
     
    加工性能
     
    热加工
     
    925合金的热加工炉温是1600-2150°F。为达到最高强度和耐腐蚀性能,热加工的温度范围是1600-1800°F。
     
    机加
     
    925合金的固溶态和时效态都有很好的机加性能。为达到最好的成品光洁度,可以在固溶处理后进行粗加工,然后进行时效,然后再进行精加工。
     
    焊接
     
    925合金可用钨极气体保护焊